HY114Cast copper repair agent
HY114 copper repair agent is used for the repair of casting defects of various copper castings, and the repair and regeneration of wear and scratches of copper parts.
Product details
HY114 copper repair agent is used for the repair of casting defects of various copper castings, and the repair and regeneration of wear and scratches of copper parts.
Instructions
1. Surface treatment: Grind and roughen the surface to be repaired to a depth of more than 1mm and then clean it with HY755 cleaning agent or acetone. The surface to be trimmed must be clean, free of water and oil.
2 Mixing: Weigh components A and B according to the specified weight ratio, and mix them thoroughly to make the color completely consistent.
3 Coating: Use a rubber knife to apply the matched steel repair agent to the surface to be repaired. You can apply a small amount first, press it repeatedly with a rubber knife, and then apply the remaining repair agent after fully infiltrating, leaving a margin for processing.
4. Curing: After curing at room temperature for 12 hours, all kinds of mechanical processing can be carried out. When the ambient temperature is lower than 15 ℃, the curing time can be appropriately extended. Holding at 80℃ for 3 hours can shorten the curing time and obtain better coating properties.
Product specifications: 500g/set, 12 sets/box.
Instructions
1. Surface treatment: Grind and roughen the surface to be repaired to a depth of more than 1mm and then clean it with HY755 cleaning agent or acetone. The surface to be trimmed must be clean, free of water and oil.
2 Mixing: Weigh components A and B according to the specified weight ratio, and mix them thoroughly to make the color completely consistent.
3 Coating: Use a rubber knife to apply the matched steel repair agent to the surface to be repaired. You can apply a small amount first, press it repeatedly with a rubber knife, and then apply the remaining repair agent after fully infiltrating, leaving a margin for processing.
4. Curing: After curing at room temperature for 12 hours, all kinds of mechanical processing can be carried out. When the ambient temperature is lower than 15 ℃, the curing time can be appropriately extended. Holding at 80℃ for 3 hours can shorten the curing time and obtain better coating properties.
Product specifications: 500g/set, 12 sets/box.